316 Paslanmaz Çelik Levha

Buradasınız: Ev -> Ürünler -> Paslanmaz Çelik Levha -> 316 Paslanmaz Çelik Levha
Biz teknik bir Taiwan 316 Paslanmaz Çelik Levha üreticisi, fabrika, tedarikçi ve ihracatçı .Bağlı olarak istikrarlı yatırım , üstün yeterlilik ve iyi satış sonrası hizmet sektöründe önde gelen üretici ve ihracatçılarından biri olarak bize yaptık . Biz kaliteli ürün ve rekabetçi fiyat ve zamanında teslimat sizin için söz veriyorum. Biz müşterilerimiz ile uzun vadeli iş kurmak olmuştur. Eğer ürünlerimizden herhangi modeli ilgilenen varsa , lütfen bize ulaşın contact us.
  • 316 Paslanmaz Çelik Levha

Modeli:
316 Paslanmaz Çelik Levha
Specifications
Article316 Cold Rolled stainless steel plate
StandardAISI, ASTM, GB, JIS
Widthas your requirement
SurfaceBA
typePlate / Strip / Sheet / Coil
Thickness0.4mm; 0.5mm; 0.6mm; 0.7mm; 0.8mm; 0.9mm; 1.0mm; 1.1mm; 1.2mm; 1.3mm; 1.4mm; 1.5mm; 1.6mm; 1.7mm; 1.8mm; 1.9mm; 2.0mm~4.0mm
UsageCold-rolled, bright annealed and skin passed products with extremely good surface glossiness and high reflectivity, are used in building decoration, home appliance product and kitchen installation, etc.
Parkingwooden packing or
PaymentSmall quantity:T/T at sight,30% in advance ,70% after receiving the B/L cop; Large quantity:L/C at sight
Delivery Time15days after received T/T or L/C

SUS316 chemical composition:
ElementsCSiMnPSCrNiMo
Specification0.081.002.000.0450.03016.00-18.0010.00-14.002.00-3.00

316/316L is an austenitic stainless steel enhanced with an addition of 2.5% lybdenum, to provide superior corrosion resistance to 304 stainless steel. 316/316L has improved pitting corrosion resistance and has excellent resistance to sulphates, phosphates and other salts.

316/316L has better resistance than standard 18/8 types to sea water, reducing acids and solution of chlorides, bromides and iodies.

Types 316 and 316L Stainless Steels exhibit better corrosion resistance than Type 304. They provide excellent resistance to pitting type corrosion such as encountered in a sea coast environment. They also provide good resistance to most chemicals involved in the paper, textile and photographic industries.
They are particularly useful in one to five percent sulfuric acid solutions up to 150°F (66°C) as well as acetic, phosphoric, formic and tartaric acids, and in certain chloride, bromide and iodide solutions.

Corrosion Resistance:
Types 316 and 316L Stainless Steels exhibit better corrosion resistance than Type 304. They provide excellent resistance to pitting type corrosion such as encountered in a sea coast environment. They also provide good resistance to most chemicals involved in the paper, textile and photographic industries.
They are particularly useful in one to five percent sulfuric acid solutions up to 150°F (66°C) as well as acetic, phosphoric, formic and tartaric acids, and in certain chloride, bromide and iodide solutions.

Oxidation Resistance:
The maximum temperature to which Types 316 and 316L can be exposed continuously without appreciable scaling is about 1700°F (927°C). For intermittent exposure, the maximum exposure temperature is about 1600°F (871°C).

Heat Treatments:
Types 316 and 316L are non-hardenable by heat treatment. Annealing: Heat to 1900- 2100°F (1038- 1149°C), then rapidly quench.

Cold Working:
Due to the higher nickel content, these grades work harden at a lower rate than Type 304. In the annealed condition, they exhibit excellent ductility and may be readily roll formed, deep drawn, and bent. is essential to restore ductility and to lower hardness for subsequent forming operations. Severely formed parts should be annealed to remove stresses.

Formability:
Types 316 and 316L can be readily formed and drawn.


Şimdi Sorgulama +Şimdi Sorgulama -