Vi är ett tekniskt Taiwan 316 rostfri plåt tillverkare, fabriken, leverantör och exportör. Beroende på stabilt investeringsklimat, överlägsen kompetens och god efter köp har vi gjort oss som ett av de ledande tillverkare och exportörer i branschen. Vi lovar kvalitet och konkurrenskraftiga priser och på leverans i tid för dig. Vi har skapa ett långsiktigt affärer med våra kunder. Om du är intresserad av någon modell av våra produkter, vara fria att kontakta oss.
  • 316 rostfri plåt

modell:
316 rostfri plåt
Specifications
Article316 Cold Rolled stainless steel plate
StandardAISI, ASTM, GB, JIS
Widthas your requirement
SurfaceBA
typePlate / Strip / Sheet / Coil
Thickness0.4mm; 0.5mm; 0.6mm; 0.7mm; 0.8mm; 0.9mm; 1.0mm; 1.1mm; 1.2mm; 1.3mm; 1.4mm; 1.5mm; 1.6mm; 1.7mm; 1.8mm; 1.9mm; 2.0mm~4.0mm
UsageCold-rolled, bright annealed and skin passed products with extremely good surface glossiness and high reflectivity, are used in building decoration, home appliance product and kitchen installation, etc.
Parkingwooden packing or
PaymentSmall quantity:T/T at sight,30% in advance ,70% after receiving the B/L cop; Large quantity:L/C at sight
Delivery Time15days after received T/T or L/C

SUS316 chemical composition:
ElementsCSiMnPSCrNiMo
Specification0.081.002.000.0450.03016.00-18.0010.00-14.002.00-3.00

316/316L is an austenitic stainless steel enhanced with an addition of 2.5% lybdenum, to provide superior corrosion resistance to 304 stainless steel. 316/316L has improved pitting corrosion resistance and has excellent resistance to sulphates, phosphates and other salts.

316/316L has better resistance than standard 18/8 types to sea water, reducing acids and solution of chlorides, bromides and iodies.

Types 316 and 316L Stainless Steels exhibit better corrosion resistance than Type 304. They provide excellent resistance to pitting type corrosion such as encountered in a sea coast environment. They also provide good resistance to most chemicals involved in the paper, textile and photographic industries.
They are particularly useful in one to five percent sulfuric acid solutions up to 150°F (66°C) as well as acetic, phosphoric, formic and tartaric acids, and in certain chloride, bromide and iodide solutions.

Corrosion Resistance:
Types 316 and 316L Stainless Steels exhibit better corrosion resistance than Type 304. They provide excellent resistance to pitting type corrosion such as encountered in a sea coast environment. They also provide good resistance to most chemicals involved in the paper, textile and photographic industries.
They are particularly useful in one to five percent sulfuric acid solutions up to 150°F (66°C) as well as acetic, phosphoric, formic and tartaric acids, and in certain chloride, bromide and iodide solutions.

Oxidation Resistance:
The maximum temperature to which Types 316 and 316L can be exposed continuously without appreciable scaling is about 1700°F (927°C). For intermittent exposure, the maximum exposure temperature is about 1600°F (871°C).

Heat Treatments:
Types 316 and 316L are non-hardenable by heat treatment. Annealing: Heat to 1900- 2100°F (1038- 1149°C), then rapidly quench.

Cold Working:
Due to the higher nickel content, these grades work harden at a lower rate than Type 304. In the annealed condition, they exhibit excellent ductility and may be readily roll formed, deep drawn, and bent. is essential to restore ductility and to lower hardness for subsequent forming operations. Severely formed parts should be annealed to remove stresses.

Formability:
Types 316 and 316L can be readily formed and drawn.


Förfrågan nu +Förfrågan nu -
Vår expertis har det möjligt för oss att säkerställa bästa 316 rostfri plåt genom att utsätta våra produkter till stränga åtgärder för kvalitetskontroll under varje etapp av produktionen och samtidigt leverans. Vi hjärtligt välkomna alla relevanta vänner över hela världen kommer för besök och samarbete!