Stainless Steel Strips

You are here: Home -> Products -> Stainless Steel Strip -> Stainless Steel Strips
YES Stainless Co.,Ltd. is the leading manufacturer, supplier and exporter of Stainless Steel Strips in Taiwan which are designed using high grade raw material that is sourced from our respected vendor base, having years of experience in the market. In addition to manufacturing them in standard dimensions, we also offer our customers the option of customizing these products as per their specific requirements. Our produce is available at very reasonable prices.
  • Stainless Steel Strips

Model:
Stainless Steel Strips
Specifications
Article304 Cold Rolled stainless steel strip
StandardAISI, ASTM, GB, JIS
Widthas your requirement
SurfaceBA
typePlate / Strip / Sheet / Coil
Thickness0.4mm; 0.5mm; 0.6mm; 0.7mm; 0.8mm; 0.9mm; 1.0mm; 1.1mm; 1.2mm; 1.3mm; 1.4mm; 1.5mm; 1.6mm; 1.7mm; 1.8mm; 1.9mm; 2.0mm~4.0mm
UsageCold-rolled, bright annealed and skin passed products with extremely good surface glossiness and high reflectivity, are used in building decoration, home appliance product and kitchen installation, etc.
Parkingwooden packing or as your requirement
PaymentSmall quantity: T/T at sight, 30% in advance , 70% after receiving the B/L cop ; Large quantity:L/C at sight
Delivery Time15days after received T/T or L/C

SUS304 chemical composition:
ElementsCSiMnPSCrNi
Specification0.081.002.000.0450.03018.0-20.08.00-10.50

The maximum temperature to which Type 304 can be exposed continuously without appreciable scaling is about 1650°F (899°C). For intermittent exposure, the maximum exposure temperature is about 1500°F (816°C).

Type 304 is non-hardenable by heat treatment. Annealing: Heat to 1900 - 2050°F (1038 - 1121°C), then cool rapidly.
Thin strip sections may be air cooled, but heavy sections should be water quenched to minimize exposure in the carbide precipitation region.
Stress Relief Annealing: Cold worked parts should be stress relieved at 750°F (399°C) for 1/2 to 2 hours.

Type 304 Stainless Steel is a variation of the basic 18-8 grade, Type 302, with a higher chromium and lower carbon content.
Its lower carbon minimizes chromium carbide precipitation due to welding and its susceptibility to intergranular corrosion.
In many instances, Type 304 can be used in the “as-welded” condition, while Type 302 must be annealed in order to retain adequate corrosion resistance.