www.stainlesssteelmetal.net especializa-se na fabricação, fornecendo e exportando a Perfuração de aço inoxidável, com uma fábrica em Taiwan.Foi sempre nosso foco para manufaturar a produtos qualidade superior e para entregá-los como por a programação.Nosso espírito inovativo permite-nos de ir antes de nossos concorrentes equipados com as facilidades de teste as mais avançadas da produtos.Os inquéritos dos atacadistas, dos distribuidores, dos compradores, dos agentes e da produtos globais OEM/ODM da são dados boas-vindas.
  • Perfuração de aço inoxidável

Modelo:
Perfuração de aço inoxidável
Austenitic Grades
Austenitic grades are those alloys which are commonly in use for stainless applications. The austenitic grades are not magnetic. The most common austenitic alloys are ironchromium-nickel steels and are widely known as the 300 series. The austenitic stainless steels, because of their high chromium and nickel content, are the most corrosion resistant of the stainless group providing unusually fine mechanical properties. They cannot be hardened by heat treatment, but can be hardened significantly by cold-working.

Straight Grades
The straight grades of austenitic stainless steel contain a maximum of.08% carbon. There is a misconception that straight grades contain a minimum of.03%, but the specStainless.

"L" Grades
The "L" grades are used to provide extra corrosion resistance after welding.The letter "L" after a stainless steel type indicates low (as in 304L). The is kept to0.03% or under to avoid carbide precipitation. Carbon in steel when heated to temperatures in what is called the critical range (800 degrees F to 1600 degrees F) precipitates out, combines with the chromium and gathers on the grain boundaries. This deprives the steel of the chromium in solution and promotes corrosion adjacent to the grain boundaries.

By controlling the amount of carbon, this is minimized. For weldability, the "L" grades are used. You may ask why all stainless steels are not produced as "L" grades. There are a couple of reasons. First, the "L" grades are more expensive. In addition, carbon, at high temperatures imparts great physical strength Frequently the mills are buying their raw material in "L" grades, but specifying the physical properties of the straight grade to retain straight grade strength. A case of having your cake and heating it too.This results in the material being dual certified 304/304L; 316/316L, etc.

"H" Grades
The "H" grades contain a minimum of.04% carbon and a maximum of.10% carbon and are designated by the letter "H" after the alloy. People ask for "H" grades primarily when the material will be used at extreme temperatures as the higher carbon helps the material  retain strength at extreme temperatures. You may hear the phrase "solution annealing". This means only that the carbides which
may have precipitated (or moved) to the grain boundaries are put back into solution (dispersed) into the matrix of the metal by the annealing process. "L" grades are used where annealing after welding is impractical, such as in the field where pipe and fittings are being welded.

Inquérito agora +Inquérito agora -
Nossa perícia tiver permitir-nos de assegurar a Perfuração de aço inoxidável sujeitando nossa produtos medidas de controle estritas da qualidade durante cada estágio de produção e quando expedição.Nós damos boas-vindas sincera a todos os amigos relevantes pelo mundo inteiro para vir para a visita e a cooperação!